Polymaker PolyMide PA6-CF 2.0kg 1.75mm 3D Printing Filament - Industrial Range
Polymaker PolyMide PA6-CF 2.0kg 1.75mm 3D Printing Filament - Packaging
3D Printing Pro

Polymaker PolyMide PA6-CF 2.0kg 1.75mm 3D Printing Filament - Industrial Range

Regular price $299.00

Polymaker PolyMide PA6-CF 

PolyMide™ is a family of Nylon/polyamide based filaments. Produced with Polymaker’s Warp-Free™ technology, PolyMide™ filaments deliver engineering properties intrinsic to Nylon and ease of printing.

PolyMide™ PA6-CF is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.

PolyMide™ PA6 CF features Polymaker's Warp-Free™ technology and Fiber Adhesion™ technology:

Warp-Free™ technology enables the production of Nylon-based filaments that can be 3D printed with excellent dimensional stability and near-zero warpage. This is achieved by the fine control of microstructure and crystallization behavior of Nylon, which enables the material to fully release the internal stress before solidification.

Fiber Adhesion™ technology improves the layer adhesion of fiber reinforced materials, by optimizing the surface chemistry of the fibers to achieve better dispersion and bonding to the matrix. This results in better strength along the Z-axis and reduced mechanical anisotropy.

RECOMMENDED SETTINGS

Nozzle Temperature:
280˚C – 300˚C *

Printing Speed:
60mm/s

Bed Temperature:
25˚C – 50˚C (Do NOT exceed 50 ˚C)

Bed Surface:
almost any surface with a thin coat of PVA glue or Magigoo PA

Cooling Fan:
OFF

MECHANICAL PROPERTIES

Young’s Modulus:
7453 ± 656 (MPa)

Tensile Strength:
105.0 ± 5.0 (MPa)

Bending Strength:
169.0 ± 4.7 (MPa)

Charpy Impact Strength:
13.34 ± 0.52 (kJ/m2)

THERMAL PROPERTIES

Heat Deflection Temperature
(ISO 75 1.8 MPa):
196 ˚C

Heat Deflection Temperature
(ISO 75 0.45 MPa):
215 ˚C

Melting Temperature:
220 (°C)

 